The microstructure and microhardness of Sn-xAg and Sn-xCu solders were investigated as functions of alloy composition and cooling rate. The Ag compositions examined varied from 0.5 to 3.5 wt %, while Cu varied from 0.5 to 2.0 wt %. Three cooling rates were employed during solidification; 0.02 °C/s (furnace-cooling), about 10 °C/s (air-cooling), and 100 °C/s or higher (rapid-solidification). Sn grain size and orientation were observed by cross polarization light microscopy and Electron Backscattering Diffraction (EBSD) techniques. The microhardness was measured to correlate the mechanical properties with alloy compositions and cooling rates. From this study, it was found that both alloy composition and cooling rate can significantly affect the Sn grain size and hardness in Sn-rich solders. The critical factors that affect the microstructure-property relationships of Sn-rich solders are discussed, which include grain size, crystal orientation, dendrite cells, twin boundaries, intermetallic compounds (IMC), among others.
By: Sun-Kyoung Seo; Sung K. Kang; Da-Yuan Shih; Hyuck Mo Lee
Published in: RC24581 in 2008
LIMITED DISTRIBUTION NOTICE:
This Research Report is available. This report has been submitted for publication outside of IBM and will probably be copyrighted if accepted for publication. It has been issued as a Research Report for early dissemination of its contents. In view of the transfer of copyright to the outside publisher, its distribution outside of IBM prior to publication should be limited to peer communications and specific requests. After outside publication, requests should be filled only by reprints or legally obtained copies of the article (e.g., payment of royalties). I have read and understand this notice and am a member of the scientific community outside or inside of IBM seeking a single copy only.
Questions about this service can be mailed to reports@us.ibm.com .